| Categories | Polyaspartic Polyurea Resin |
|---|---|
| Brand Name: | Zhuhai Feiyang |
| Model Number: | F330 |
| Certification: | REACH,ISO 9001-2015, ISO 14001-2015 |
| Place of Origin: | Zhuhai, China |
| MOQ: | 200kg |
| Payment Terms: | L/C, T/T |
| Supply Ability: | More than 20000 tons per year |
| Delivery Time: | 7days after order comfirmed |
| Packaging Details: | 200KG/Drum, 4Drums/pallet, 16Ton/20GP |
| Model: | F330 |
| Color: | Colorless to light yellow green transparent liquid |
| Amine value(mg KOH/g): | 165-185 |
| Equivalent weight(g/mol): | 334 |
| Viscosity: | 250-600 |
| Feature: | High elongation and high Elastic |
| Company Info. |
| SHENZHEN FEIYANG PROTECH CORP.,LTD |
| Verified Supplier |
| View Contact Details |
| Product List |
FEISPARTIC F330 Floor Coatings Elastic Polyaspartic Polyurea Resin
1. Model: F330
● Chemical Name: Aspartic Acid, Polyaspartic Polyurea Resin
2. Properties and application
●FEISPARTIC F330 is a high solid and low viscosity resin; viscosity is as low as 200mPa.s, it can be made into high-solid low, viscosity environmental protection coatings.
●FEISPARTIC F330 has moderate reactivity and can prolong polyurea hand brush construction time.
●The film made of FEISPARTIC F330 has excellent elastic resilience, flow, gloss, and touch.
●FEISPARTIC F330 can react with our flexible curing agent to make excellent mechanical properties elastic material; the elongation can reach 400%.
3. Main Feature
1. F330 could make good elastic resilience solvent-free floor
coatings.
2. F330 could be used to produce high elongation and high elastic
waterproof coating.
3. F330 could be used to produce solvent-free adhesives and sealing
material.
| INDEX | VALUE |
| Appearance | Colorless to light yellow green transparent liquid |
| Hazen (Pt-Co) | ≤250 |
| Solid Content(％) | 97±2 |
| Amine value(mg KOH/g) | 165～185 |
| Amine Equivalent(g/mol) | 334 |
| Equivalently hydroxy content(%) | 5.09 |
| Viscosity(mpa.s/25℃) | 250～600 |
| Relative density (25℃) | 1.06±0.02 |
6. Polyaspartic Property Advantage
| Property | Polyaspartic polyurea | Conventional polyurethane | Spray polyurea |
| Environmental property | Environmental friendly, construction solid content 70%-100% | Poor environmental protection, construction solid content 30%-40% | Good environmental protection, construction content 100% |
| Reaction speed | Curing time adjustive,20min-4h, normally cure in 15-℃ | Low reaction speed, request curing temperature above 5-℃, curing time more than 24h in normal temperature | Rapid curing speed, from seconds to tens of seconds |
| Adhesion with substrate | Don’t need primer; the adhesion with carbon steel substrate is beyond 14Mpa, and the bonding with concrete reaches 4.5Mpa. | Need primer, adhesion with carbon steel substrate less than 8MPa, bonding with concrete is 2.5 Mpa. | Need primer, low adhesion |
| Weather resistance | QUVA test reaches 4000h | QUVA test is 1000h at most | Poor weather resistance, QUVA ＜200h |
| Film thickness | One-time construction film 50μm—1mm | One-time construction film 50μm——100μm | One-time construction film 0.6mm-2mm |
| Mechanical properties | Rigidity hardness 2H,elongation 400%, tensile strength 25MP | Rigidity hardness 2H,elongation 400%, tensile strength 3MPa | Same as aspartic polyurea |
| Construction | Multiple construction methods get rid of the restriction of specified equipment. | Same as aspartic polyurea | Relying on sizeable special equipment |
Learn polyaspartic knowledge: Polyaspartic FAQ
|